Nanovia PETG CF : Carbon fiber reinforced

Starting at : 64,40 € ex. VAT/ kg

Very easy to 3D print, Nanovia PETG CF is printable without a heated enclosure and allows for the creation of functional parts useable up to 80 °C, suitable for an outdoor usage. Thanks to the incorporation of carbon fibers, this FFF 3D printer filament allows for good mechanical properties, rigidity, and dimensional control during the realization of technical parts.

Diameter

1.75 mm

2.85 mm

Weight

500 g

2000 g

sample

Clear

SKU: N/A Categories: 3D printing filament, Aéronautique, Carbon fibre, Défense, Material, PETg (Polyethylene terephthalate)

Description
Additional information

Description

Properties

3D Printing

Extrusion temperature	220 – 240	°C
Plate temperature	80 – 90	°C
Enclosure temperature	20	°C
Nozzle (minimal)	0.5	mm
Printing Speed	20 – 60	mm/s
Diameter	1.75 & 2.85	mm	+/- 50 µm
Colour	Black

Mechanical properties

Density

1.35

g/cm³

ISO 1183

Tensile

Test performed at 1mm/min on 3D printed test specimins at 0°, along with the tension stress.

Young’s modulus	5800	MPa	ISO 527-2/1A
Ultimate strength	57	MPa	ISO 527-2/1A
Elongation ultimate strength	2.3	%	ISO 527-2/1A

Comparison of Nanovia PETG CF improved tensile resistance compared to native PETG

Impact

Charpy (notched)

kJ/m²

Thermal properties

°C

Documentation

Download the technical chart Download the security chart

last updated : 08/03/2023

nanovia petg cf utilisé par les armées françaises

Nanovia PETg CF allows for the creation of structural 3D prints with low warping thanks to its compound carbon fibers structure. This composite 3D filament has been specially designed to be compatible with standard 3D printers equipped with a heated bed.