Nanovia Mt : Stainless steel 316L

Print dense stainless steel pieces with a standard 3D printer and a sintering step without chemical debinding.
Ask for a quote

Category: Tag:

Description

Properties

3D Printing

Extrusion T°170 – 190 °C
Plate T°40 – 60 °C
Enclosure T°ambiant
Nozzle>0,6 mm
Printing speed20 – 40 mm/s
Extrusion debit1,14
Diameters1,75 & 2,85 mm +/- 50 µm
Linear Weight10.00 g/m @ Ø 1,75
26.52 g/m @ Ø 2,85
ColourGray

Mechanical Properties

Density4.15 g/cm3 (ISO 1183)
Shrinkage after sintering10 – 15 %

Documentation

Download the technical chart

Printable using standard 3D FDM printers and not brittle in its filament form, create stainless steel (316L grade) pieces using our new Nanovia Mt Inox 316L filament.

Thanks to its patented formula, the printed parts can be directly sintered without any chemical debinding steps beforehand.

Before sintering, it’s possible to apply standard post treatment much like a plastic 3D prints, even tool the piece without requiring any specialized equipment.

After sintering you’ll be left with a 100% stainless steel part.

Avantages:

  • Create metallic parts with all the advantages of 3D printing techniques.
  • Easy post treatment before sintering.
  • No chemical debindings tep before sintering.
  • An alternative/complement to traditional substractive prodution methodes.

Application recommendations

post traitement simple d'une pièce imprimé Nanovia Mt Inox 316L verte avant frittage

Storage

  • It’s recommended to store Nanovia Mt 316l in a dry location
  • Pour assurer une parfaite impression, il est conseillé d’étuver votre filament à 60 °C pendant 6h ou plus, lorsque la bobine a été exposée à l’air libre pendant une longue période.

Printing

With it’s close to standard printer settings, Nanovia MT Inox 316l is useable on most commercially available 3D FDM printers.

  • Extrusion temperature : 170 à 190 °C
  • Plate temperature : 40 à 60 °C
  • In order to protect your equipment we recommend using a nozzle adapted for abrasive materials.

Post treatment

  • It’s possible to apply tradional post treatment methods on the green (not yet cintered) 3D printed pieces, such as sanding, polishing, tapering, drilling, tooling etc…

Sintering

The sintering of Nanovia Mt Inox 316L happens in two consecutive steps :

  • Debinding on a relative low temperature around 400 °C
  • Sintering at 1180°C
Grafique de deliantage et de frittage du nanovia mt inox 316L
Time (min)20150300360500530850
Temperature (°C)30038038043043011801180
  • It’s possible to sinter Nanovia Mt in an SDS sintering oven.
  • It is required to bury / cover the green parts in alumina powder filled crucible during the thermal debinding phase.
  • Add a fine layer of carbon powder to capture the released oxygen, or sinter using an inert atmosphere such as argon.

Health & safety

Sintering

  • Please refer to the product’s MSDS, as well as your sintering oven’s manuel.

Packaging

Spools are packed in individual boxes, sous-vide with desiccant. Spools are equipped with both a material traciblity and a production series number.

SpoolL1L2D1D2D3
500g554520010552
2kg1009030021052